PCL vs. PCTFE
Both PCL and PCTFE are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is PCL and the bottom bar is PCTFE.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.2 | |
| 1.4 |
| Elongation at Break, % | 300 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 10 | |
| 36 |
Thermal Properties
| Glass Transition Temperature, °C | -60 | |
| 100 |
| Maximum Temperature: Decomposition, °C | 200 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 40 | |
| 150 |
| Melting Onset (Solidus), °C | 60 | |
| 220 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.1 | |
| 2.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.61 | |
| 0.37 |
| Stiffness to Weight: Bending, points | 32 | |
| 17 |
| Strength to Weight: Axial, points | 2.5 | |
| 4.6 |
| Strength to Weight: Bending, points | 9.4 | |
| 11 |