PCL vs. UP
PCL belongs to the thermoplastics classification, while UP belongs to the thermoset plastics. There are 9 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is PCL and the bottom bar is UP.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 2.0 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.2 | |
| 17 |
| Elongation at Break, % | 300 | |
| 1.0 |
| Glass Transition Temperature, °C | -60 | |
| 60 |
| Stiffness to Weight: Axial, points | 0.61 | |
| 4.7 |
| Stiffness to Weight: Bending, points | 32 | |
| 43 |
| Strength to Weight: Axial, points | 2.5 | |
| 4.2 |
| Strength to Weight: Bending, points | 9.4 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 10 | |
| 30 |