PC vs. LCP
Both PC and LCP are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is PC and the bottom bar is LCP.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.2 to 1.4 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 3.5 to 110 | |
| 1.0 to 3.0 |
| Flexural Modulus, GPa | 2.3 to 10 | |
| 9.0 to 23 |
| Flexural Strength, MPa | 92 to 160 | |
| 160 to 320 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 130 to 150 | |
| 240 to 270 |
| Specific Heat Capacity, J/kg-K | 1000 to 1200 | |
| 1020 to 1200 |
| Strength to Weight: Axial, points | 15 to 30 | |
| 33 to 43 |
| Strength to Weight: Bending, points | 30 to 45 | |
| 45 to 56 |
| Tensile Strength: Ultimate (UTS), MPa | 66 to 160 | |
| 180 to 230 |