PC vs. PA 6/10
Both PC and PA 6/10 are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is PC and the bottom bar is PA 6/10.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.2 to 1.4 | |
| 1.1 |
| Elongation at Break, % | 3.5 to 110 | |
| 110 to 120 |
| Flexural Modulus, GPa | 2.3 to 10 | |
| 1.4 to 2.0 |
| Flexural Strength, MPa | 92 to 160 | |
| 48 to 59 |
| Impact Strength: Notched Izod, J/m | 140 to 440 | |
| 85 |
| Specific Heat Capacity, J/kg-K | 1000 to 1200 | |
| 1510 |
| Strength to Weight: Axial, points | 15 to 30 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 30 to 45 | |
| 25 to 30 |
| Tensile Strength: Ultimate (UTS), MPa | 66 to 160 | |
| 45 to 60 |