PCTFE vs. NEMA Laminate
PCTFE belongs to the thermoplastics classification, while NEMA laminate belongs to the thermoset plastics. There are 12 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is PCTFE and the bottom bar is NEMA laminate.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 38 | |
| 190 to 360 |
| Flexural Modulus, GPa | 1.2 | |
| 6.4 to 18 |
| Flexural Strength, MPa | 59 | |
| 87 to 340 |
| Impact Strength: Notched Izod, J/m | 160 | |
| 20 to 430 |
| Tensile Strength: Ultimate (UTS), MPa | 36 | |
| 55 to 260 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 150 | |
| 120 to 200 |
| Thermal Expansion, µm/m-K | 130 | |
| 9.0 to 20 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 21 | |
| 12 to 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.1 | |
| 1.3 to 1.9 |
| Water Absorption After 24 Hours, % | 0.0094 | |
| 0.17 to 3.5 |
Common Calculations
| Strength to Weight: Axial, points | 4.6 | |
| 8.3 to 40 |
| Strength to Weight: Bending, points | 11 | |
| 17 to 50 |