CVD Diamond vs. Machinable Glass-ceramic
CVD diamond belongs to the non-oxide engineering ceramics classification, while machinable glass-ceramic belongs to the glass and glass-ceramics. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is CVD diamond and the bottom bar is machinable glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1050 | |
| 67 |
| Fracture Toughness, MPa-m1/2 | 5.5 | |
| 2.5 |
| Poisson's Ratio | 0.1 | |
| 0.29 |
| Tensile Strength: Ultimate (UTS), MPa | 750 | |
| 84 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 500 | |
| 790 |
| Thermal Conductivity, W/m-K | 1900 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 1.0 | |
| 21 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 5.7 | |
| 6.4 |
| Electrical Dissipation At 1 MHz | 0.00020 | |
| 0.0050 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.5 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 170 | |
| 14 |
| Stiffness to Weight: Bending, points | 96 | |
| 51 |
| Strength to Weight: Axial, points | 59 | |
| 8.8 |
| Strength to Weight: Bending, points | 52 | |
| 16 |
| Thermal Diffusivity, mm2/s | 1080 | |
| 0.56 |
| Thermal Shock Resistance, points | 51 | |
| 4.3 |