PES vs. PTFE

Both PES and PTFE are thermoplastics. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is PES and the bottom bar is PTFE.

Polyethersulfone (PES)Polytetrafluoroethylene (PTFE)

Metric UnitsUS Customary Units

Mechanical Properties

Elongation at Break, %		65
Elongation at Break, %		75 to 300

Flexural Modulus, GPa		2.6
Flexural Modulus, GPa		0.4 to 1.3

Flexural Strength, MPa		130
Flexural Strength, MPa		13 to 50

Tensile Strength: Ultimate (UTS), MPa		87
Tensile Strength: Ultimate (UTS), MPa		13 to 25

Thermal Properties

Heat Deflection Temperature At 1.82 MPa (264 psi), °C		200
Heat Deflection Temperature At 1.82 MPa (264 psi), °C		66 to 70

Maximum Temperature: Mechanical, °C		200
Maximum Temperature: Mechanical, °C		260 to 270

Thermal Conductivity, W/m-K		0.18
Thermal Conductivity, W/m-K		0.24 to 0.65

Thermal Expansion, µm/m-K		53
Thermal Expansion, µm/m-K		110 to 120

Electrical Properties

Dielectric Constant (Relative Permittivity) At 1 MHz		3.5
Dielectric Constant (Relative Permittivity) At 1 MHz		2.1 to 2.4

Electrical Dissipation At 1 MHz		0.0035
Electrical Dissipation At 1 MHz		0.00017 to 0.050

Electrical Resistivity Order of Magnitude, 10^x Ω-m		15
Electrical Resistivity Order of Magnitude, 10^x Ω-m		2.0 to 18

Otherwise Unclassified Properties

Density, g/cm³		1.4
Density, g/cm³		2.1 to 2.3

Limiting Oxygen Index (LOI), %		36
Limiting Oxygen Index (LOI), %		90

Water Absorption After 24 Hours, %		0.34
Water Absorption After 24 Hours, %		0.0093 to 0.050

Common Calculations

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		1.7 to 3.2

Strength to Weight: Bending, points		32
Strength to Weight: Bending, points		5.7 to 8.7