PMP vs. POM-C
Both PMP and POM-C are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is PMP and the bottom bar is POM-C.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 0.83 | |
| 1.4 to 1.6 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.1 | |
| 2.8 to 9.7 |
| Elongation at Break, % | 30 | |
| 3.0 to 65 |
| Impact Strength: Notched Izod, J/m | 130 | |
| 68 to 69 |
| Specific Heat Capacity, J/kg-K | 1750 | |
| 1130 to 1370 |
| Stiffness to Weight: Axial, points | 0.74 | |
| 1.1 to 3.3 |
| Stiffness to Weight: Bending, points | 41 | |
| 33 to 44 |
| Strength to Weight: Axial, points | 8.0 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 22 | |
| 24 to 32 |
| Tensile Strength: Ultimate (UTS), MPa | 24 | |
| 61 to 110 |