PPSU vs. CAP
Both PPSU and CAP are thermoplastics. There are 18 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is PPSU and the bottom bar is CAP.
Metric UnitsUS Customary Units
Mechanical Properties
Elongation at Break, % | 26 | |
35 to 50 |
Flexural Modulus, GPa | 4.7 | |
1.2 to 1.9 |
Flexural Strength, MPa | 130 | |
29 to 56 |
Tensile Strength: Ultimate (UTS), MPa | 95 | |
28 to 45 |
Thermal Properties
Glass Transition Temperature, °C | 220 | |
190 |
Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 210 | |
65 to 80 |
Heat Deflection Temperature At 455 kPa (66 psi), °C | 220 | |
75 to 90 |
Specific Heat Capacity, J/kg-K | 970 | |
1480 |
Thermal Conductivity, W/m-K | 0.24 | |
0.25 |
Thermal Expansion, µm/m-K | 45 | |
14 |
Electrical Properties
Dielectric Constant (Relative Permittivity) At 1 MHz | 3.4 | |
3.6 |
Dielectric Strength (Breakdown Potential), kV/mm | 16 | |
15 |
Electrical Resistivity Order of Magnitude, 10x Ω-m | 14 | |
16 |
Otherwise Unclassified Properties
Density, g/cm3 | 1.4 | |
1.2 |
Water Absorption After 24 Hours, % | 0.44 | |
1.4 to 1.7 |
Common Calculations
Strength to Weight: Axial, points | 19 | |
6.5 to 10 |
Strength to Weight: Bending, points | 33 | |
17 to 23 |
Thermal Diffusivity, mm2/s | 0.17 | |
0.14 |