PPA vs. CAB
Both PPA and CAB are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is PPA and the bottom bar is CAB.
Metric UnitsUS Customary Units
Mechanical Properties
| Elongation at Break, % | 30 | |
| 50 to 55 |
| Flexural Modulus, GPa | 2.3 to 2.4 | |
| 0.8 to 1.7 |
| Flexural Strength, MPa | 95 to 110 | |
| 21 to 57 |
| Tensile Strength: Ultimate (UTS), MPa | 57 to 69 | |
| 20 to 50 |
Thermal Properties
| Glass Transition Temperature, °C | 92 to 130 | |
| 140 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 120 | |
| 53 to 82 |
| Specific Heat Capacity, J/kg-K | 1400 | |
| 1460 |
| Thermal Conductivity, W/m-K | 0.15 | |
| 0.25 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.1 | |
| 1.2 |
| Water Absorption After 24 Hours, % | 0.7 | |
| 1.2 to 1.6 |
Common Calculations
| Strength to Weight: Axial, points | 14 to 17 | |
| 4.8 to 12 |
| Strength to Weight: Bending, points | 29 to 33 | |
| 14 to 25 |
| Thermal Diffusivity, mm2/s | 0.095 | |
| 0.14 to 0.15 |