PP Copolymer vs. CA
Both PP copolymer and CA are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is PP copolymer and the bottom bar is CA.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 0.9 | |
| 1.3 |
| Dielectric Strength (Breakdown Potential), kV/mm | 21 to 22 | |
| 15 |
| Elongation at Break, % | 12 | |
| 25 to 30 |
| Flexural Modulus, GPa | 1.3 | |
| 1.7 to 2.1 |
| Flexural Strength, MPa | 31 | |
| 40 to 55 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 50 to 100 | |
| 65 to 75 |
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 82 to 98 | |
| 75 to 85 |
| Strength to Weight: Axial, points | 7.1 to 10 | |
| 6.4 to 7.9 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 17 to 19 |
| Tensile Strength: Ultimate (UTS), MPa | 23 to 33 | |
| 30 to 37 |