PP Copolymer vs. LCP
Both PP copolymer and LCP are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is PP copolymer and the bottom bar is LCP.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 0.9 to 1.1 | |
| 11 to 24 |
| Elongation at Break, % | 12 | |
| 1.0 to 3.0 |
| Flexural Modulus, GPa | 1.3 | |
| 9.0 to 23 |
| Flexural Strength, MPa | 31 | |
| 160 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 23 to 33 | |
| 180 to 230 |
Thermal Properties
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 50 to 100 | |
| 240 to 270 |
| Melting Onset (Solidus), °C | 150 | |
| 280 |
Otherwise Unclassified Properties
| Density, g/cm3 | 0.9 | |
| 1.4 to 1.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.56 to 0.68 | |
| 4.4 to 8.9 |
| Stiffness to Weight: Bending, points | 36 to 38 | |
| 51 to 65 |
| Strength to Weight: Axial, points | 7.1 to 10 | |
| 33 to 43 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 45 to 56 |