PP Copolymer vs. PLA
Both PP copolymer and PLA are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is PP copolymer and the bottom bar is PLA.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 0.9 to 1.1 | |
| 3.5 |
| Elongation at Break, % | 12 | |
| 6.0 |
| Flexural Modulus, GPa | 1.3 | |
| 4.0 |
| Flexural Strength, MPa | 31 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 23 to 33 | |
| 50 |
Thermal Properties
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 82 to 98 | |
| 65 |
| Maximum Temperature: Mechanical, °C | 80 | |
| 50 |
| Melting Onset (Solidus), °C | 150 | |
| 160 |
Otherwise Unclassified Properties
| Density, g/cm3 | 0.9 | |
| 1.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.56 to 0.68 | |
| 1.6 |
| Stiffness to Weight: Bending, points | 36 to 38 | |
| 40 |
| Strength to Weight: Axial, points | 7.1 to 10 | |
| 11 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 24 |