PP Copolymer vs. Thermoplastic PI
Both PP copolymer and thermoplastic PI are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is PP copolymer and the bottom bar is thermoplastic PI.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 0.9 | |
| 1.4 to 1.5 |
| Elastic (Young's, Tensile) Modulus, GPa | 0.9 to 1.1 | |
| 3.7 to 20 |
| Elongation at Break, % | 12 | |
| 1.8 to 7.5 |
| Flexural Modulus, GPa | 1.3 | |
| 3.8 to 19 |
| Flexural Strength, MPa | 31 | |
| 170 to 330 |
| Stiffness to Weight: Axial, points | 0.56 to 0.68 | |
| 1.5 to 7.9 |
| Stiffness to Weight: Bending, points | 36 to 38 | |
| 37 to 64 |
| Strength to Weight: Axial, points | 7.1 to 10 | |
| 22 to 42 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 36 to 57 |
| Tensile Strength: Ultimate (UTS), MPa | 23 to 33 | |
| 110 to 220 |