PP Homopolymer vs. HDPE
Both PP homopolymer and HDPE are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is PP homopolymer and the bottom bar is HDPE.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 0.91 to 1.2 | |
| 1.0 to 1.3 |
| Elongation at Break, % | 3.0 to 80 | |
| 2.5 to 100 |
| Flexural Modulus, GPa | 1.5 to 7.0 | |
| 4.0 to 7.5 |
| Impact Strength: Notched Izod, J/m | 42 to 95 | |
| 50 to 260 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 90 |
| Specific Heat Capacity, J/kg-K | 1230 to 1900 | |
| 1330 to 2400 |
| Strength to Weight: Axial, points | 11 to 21 | |
| 6.9 to 17 |
| Strength to Weight: Bending, points | 27 to 37 | |
| 19 to 32 |
| Tensile Strength: Ultimate (UTS), MPa | 36 to 93 | |
| 24 to 80 |
| Water Absorption At Saturation, % | 0.010 to 0.090 | |
| 0.1 to 0.3 |