PS vs. PC
Both PS and PC are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is PS and the bottom bar is PC.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.0 | |
| 1.2 to 1.4 |
| Elongation at Break, % | 1.8 to 40 | |
| 3.5 to 110 |
| Flexural Strength, MPa | 62 to 80 | |
| 92 to 160 |
| Glass Transition Temperature, °C | 100 | |
| 150 |
| Impact Strength: Notched Izod, J/m | 19 to 45 | |
| 140 to 440 |
| Specific Heat Capacity, J/kg-K | 1250 to 1400 | |
| 1000 to 1200 |
| Strength to Weight: Axial, points | 8.5 to 12 | |
| 15 to 30 |
| Strength to Weight: Bending, points | 22 to 26 | |
| 30 to 45 |
| Tensile Strength: Ultimate (UTS), MPa | 32 to 44 | |
| 66 to 160 |
| Thermal Expansion, µm/m-K | 80 to 98 | |
| 10 to 69 |