PSU vs. POM-C
Both PSU and POM-C are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is PSU and the bottom bar is POM-C.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.2 to 1.6 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 2.0 to 52 | |
| 3.0 to 65 |
| Flexural Modulus, GPa | 2.7 to 14 | |
| 2.6 to 9.0 |
| Flexural Strength, MPa | 110 to 200 | |
| 83 to 170 |
| Impact Strength: Notched Izod, J/m | 59 to 100 | |
| 68 to 69 |
| Specific Heat Capacity, J/kg-K | 910 to 1000 | |
| 1130 to 1370 |
| Strength to Weight: Axial, points | 16 to 25 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 30 to 40 | |
| 24 to 32 |
| Tensile Strength: Ultimate (UTS), MPa | 70 to 140 | |
| 61 to 110 |