PTFE vs. PHB
Both PTFE and PHB are thermoplastics. There are 11 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is PTFE and the bottom bar is PHB.
Metric UnitsUS Customary Units
Mechanical Properties
| Elongation at Break, % | 75 to 300 | |
| 7.5 |
| Flexural Strength, MPa | 13 to 50 | |
| 20 |
| Tensile Strength: Ultimate (UTS), MPa | 13 to 25 | |
| 30 |
Thermal Properties
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 66 to 70 | |
| 60 |
| Maximum Temperature: Mechanical, °C | 260 to 270 | |
| 120 |
| Melting Onset (Solidus), °C | 330 to 340 | |
| 180 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 2.0 to 18 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.1 to 2.3 | |
| 1.3 |
| Water Absorption After 24 Hours, % | 0.0093 to 0.050 | |
| 0.75 |
Common Calculations
| Strength to Weight: Axial, points | 1.7 to 3.2 | |
| 6.7 |
| Strength to Weight: Bending, points | 5.7 to 8.7 | |
| 17 |