PTFE vs. PVF
Both PTFE and PVF are thermoplastics. There are 11 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is PTFE and the bottom bar is PVF.
Metric UnitsUS Customary Units
Mechanical Properties
Flexural Strength, MPa | 13 to 50 | |
90 |
Tensile Strength: Ultimate (UTS), MPa | 13 to 25 | |
65 |
Thermal Properties
Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 66 to 70 | |
90 |
Maximum Temperature: Mechanical, °C | 260 to 270 | |
110 |
Melting Onset (Solidus), °C | 330 to 340 | |
230 |
Thermal Conductivity, W/m-K | 0.24 to 0.65 | |
0.13 |
Thermal Expansion, µm/m-K | 110 to 120 | |
100 |
Otherwise Unclassified Properties
Density, g/cm3 | 2.1 to 2.3 | |
1.4 |
Limiting Oxygen Index (LOI), % | 90 | |
23 |
Common Calculations
Strength to Weight: Axial, points | 1.7 to 3.2 | |
13 |
Strength to Weight: Bending, points | 5.7 to 8.7 | |
26 |