PTT vs. PBI
PTT belongs to the thermoplastics classification, while PBI belongs to the thermoset plastics. There are 10 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is PTT and the bottom bar is PBI.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.3 | |
| 1.3 |
| Elastic (Young's, Tensile) Modulus, GPa | 2.5 | |
| 5.9 |
| Elongation at Break, % | 60 | |
| 3.0 |
| Flexural Modulus, GPa | 2.8 | |
| 6.5 |
| Flexural Strength, MPa | 100 | |
| 220 |
| Stiffness to Weight: Axial, points | 1.0 | |
| 2.5 |
| Stiffness to Weight: Bending, points | 34 | |
| 46 |
| Strength to Weight: Axial, points | 13 | |
| 34 |
| Strength to Weight: Bending, points | 26 | |
| 50 |
| Tensile Strength: Ultimate (UTS), MPa | 60 | |
| 160 |