PVDF vs. UHMW-PE
Both PVDF and UHMW-PE are thermoplastics. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is PVDF and the bottom bar is UHMW-PE.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.1 | |
| 0.8 |
| Elongation at Break, % | 200 | |
| 400 |
| Tensile Strength: Ultimate (UTS), MPa | 49 | |
| 49 |
Thermal Properties
| Melting Onset (Solidus), °C | 170 | |
| 130 |
| Specific Heat Capacity, J/kg-K | 1120 | |
| 1750 |
| Thermal Conductivity, W/m-K | 0.12 | |
| 0.41 |
| Thermal Expansion, µm/m-K | 120 | |
| 180 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 7.5 | |
| 2.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 0.94 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.35 | |
| 0.47 |
| Stiffness to Weight: Bending, points | 20 | |
| 33 |
| Strength to Weight: Axial, points | 7.8 | |
| 14 |
| Strength to Weight: Bending, points | 17 | |
| 32 |
| Thermal Diffusivity, mm2/s | 0.061 | |
| 0.25 |
| Thermal Shock Resistance, points | 27 | |
| 25 |