Potassium Chloride vs. Machinable Glass-ceramic
Potassium chloride belongs to the non-glass optical ceramics classification, while machinable glass-ceramic belongs to the glass and glass-ceramics. There are 12 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is potassium chloride and the bottom bar is machinable glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 28 | |
| 67 |
| Poisson's Ratio | 0.18 | |
| 0.29 |
| Shear Modulus, GPa | 8.5 | |
| 26 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 690 | |
| 790 |
| Thermal Conductivity, W/m-K | 6.5 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 36 | |
| 21 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 4.6 | |
| 6.4 |
| Electrical Dissipation At 1 MHz | 0.00010 | |
| 0.0050 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.0 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 51 |
| Thermal Diffusivity, mm2/s | 4.7 | |
| 0.56 |