Quarter-hard AISI 201LN vs. Quarter-hard 80-silver 20-cadmium-oxide
Quarter-hard AISI 201LN belongs to the iron alloys classification, while quarter-hard 80-silver 20-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is quarter-hard AISI 201LN and the bottom bar is quarter-hard 80-silver 20-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.7 | |
| 9.9 |
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 70 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 64 |
| Elongation at Break, % | 28 | |
| 1.1 |
| Shear Strength, MPa | 600 | |
| 220 |
| Strength to Weight: Axial, points | 33 | |
| 11 |
| Strength to Weight: Bending, points | 27 | |
| 12 |
| Tensile Strength: Ultimate (UTS), MPa | 920 | |
| 390 |