Quarter-hard AISI 205 vs. Quarter-hard 86.5-silver 13.5-cadmium-oxide
Quarter-hard AISI 205 belongs to the iron alloys classification, while quarter-hard 86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is quarter-hard AISI 205 and the bottom bar is quarter-hard 86.5-silver 13.5-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.6 | |
| 10 |
| Elongation at Break, % | 51 | |
| 3.4 |
| Shear Strength, MPa | 700 | |
| 210 |
| Strength to Weight: Axial, points | 36 | |
| 9.9 |
| Strength to Weight: Bending, points | 29 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 980 | |
| 360 |