Quarter-hard 90-silver 10-cadmium-oxide vs. Quarter-hard S21904 Stainless Steel
Quarter-hard 90-silver 10-cadmium-oxide belongs to the otherwise unclassified metals classification, while quarter-hard S21904 stainless steel belongs to the iron alloys. There are 8 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is quarter-hard 90-silver 10-cadmium-oxide and the bottom bar is quarter-hard S21904 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 7.7 |
| Electrical Conductivity: Equal Volume, % IACS | 81 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 71 | |
| 2.9 |
| Elongation at Break, % | 3.4 | |
| 17 |
| Shear Strength, MPa | 190 | |
| 620 |
| Strength to Weight: Axial, points | 9.1 | |
| 36 |
| Strength to Weight: Bending, points | 11 | |
| 29 |
| Tensile Strength: Ultimate (UTS), MPa | 340 | |
| 1000 |