H01 C74000 Nickel Silver vs. H01 C78200 Nickel Silver
Both H01 C74000 nickel silver and H01 C78200 nickel silver are copper alloys. Both are furnished in the H01 (quarter hard) temper. They have a moderately high 92% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is H01 C74000 nickel silver and the bottom bar is H01 C78200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Rockwell B Hardness | 70 | |
| 65 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 160 |
| Melting Completion (Liquidus), °C | 990 | |
| 1000 |
| Melting Onset (Solidus), °C | 950 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 28 |
| Density, g/cm3 | 8.5 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 3.3 |
| Embodied Energy, MJ/kg | 54 | |
| 52 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 14 | |
| 14 |
| Strength to Weight: Bending, points | 15 | |
| 15 |
| Thermal Shock Resistance, points | 14 | |
| 14 |
Alloy Composition
| Copper (Cu), % | 69 to 73.5 | |
| 63 to 67 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 to 0.1 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 9.0 to 11 | |
| 7.0 to 9.0 |
| Zinc (Zn), % | 14.2 to 22 | |
| 20.2 to 28.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |