Z13004 Zinc vs. C49300 Brass
Z13004 zinc belongs to the zinc alloys classification, while C49300 brass belongs to the copper alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is Z13004 zinc and the bottom bar is C49300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 100 |
| Elongation at Break, % | 30 | |
| 4.5 to 20 |
| Poisson's Ratio | 0.25 | |
| 0.31 |
| Shear Modulus, GPa | 35 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 93 | |
| 430 to 520 |
| Tensile Strength: Yield (Proof), MPa | 76 | |
| 210 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 120 |
| Melting Completion (Liquidus), °C | 410 | |
| 880 |
| Melting Onset (Solidus), °C | 390 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 88 |
| Thermal Expansion, µm/m-K | 26 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 26 |
| Density, g/cm3 | 6.6 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.0 |
| Embodied Energy, MJ/kg | 53 | |
| 50 |
| Embodied Water, L/kg | 340 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 | |
| 21 to 71 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 33 | |
| 220 to 800 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 3.9 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 7.0 | |
| 16 to 18 |
| Thermal Diffusivity, mm2/s | 44 | |
| 29 |
| Thermal Shock Resistance, points | 2.9 | |
| 14 to 18 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0020 | |
| 0 to 0.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Bismuth (Bi), % | 0 | |
| 0.5 to 2.0 |
| Cadmium (Cd), % | 0 to 0.0030 | |
| 0 |
| Copper (Cu), % | 0 to 0.0030 | |
| 58 to 62 |
| Iron (Fe), % | 0 to 0.0030 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.0030 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 | |
| 0 to 0.030 |
| Nickel (Ni), % | 0 | |
| 0 to 1.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.2 |
| Selenium (Se), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 to 0.0010 | |
| 1.0 to 1.8 |
| Zinc (Zn), % | 99.985 to 100 | |
| 30.6 to 40.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |