SAE-AISI 1008 Steel vs. Nickel 333

SAE-AISI 1008 steel belongs to the iron alloys classification, while nickel 333 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1008 steel and the bottom bar is nickel 333.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 22 to 33
34
Fatigue Strength, MPa 150 to 220
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
81
Shear Strength, MPa 220 to 230
420
Tensile Strength: Ultimate (UTS), MPa 330 to 370
630
Tensile Strength: Yield (Proof), MPa 190 to 310
270

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1010
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 62
11
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
55
Density, g/cm3 7.9
8.5
Embodied Carbon, kg CO2/kg material 1.4
8.5
Embodied Energy, MJ/kg 18
120
Embodied Water, L/kg 45
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78 to 91
170
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 260
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 12 to 13
21
Strength to Weight: Bending, points 13 to 15
19
Thermal Diffusivity, mm2/s 17
2.9
Thermal Shock Resistance, points 10 to 12
16

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.1
Chromium (Cr), % 0
24 to 27
Cobalt (Co), % 0
2.5 to 4.0
Iron (Fe), % 99.31 to 99.7
9.3 to 24.5
Manganese (Mn), % 0.3 to 0.5
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 4.0
Nickel (Ni), % 0
44 to 48
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0
0 to 1.5
Sulfur (S), % 0 to 0.050
0 to 0.030
Tungsten (W), % 0
2.5 to 4.0