SAE-AISI 1008 Steel vs. N07776 Nickel
SAE-AISI 1008 steel belongs to the iron alloys classification, while N07776 nickel belongs to the nickel alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1008 steel and the bottom bar is N07776 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 22 to 33 | |
| 39 |
| Fatigue Strength, MPa | 150 to 220 | |
| 220 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Reduction in Area, % | 50 to 63 | |
| 57 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Shear Strength, MPa | 220 to 230 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 370 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 190 to 310 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 970 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1550 |
| Melting Onset (Solidus), °C | 1430 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 85 |
| Density, g/cm3 | 7.9 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 15 |
| Embodied Energy, MJ/kg | 18 | |
| 210 |
| Embodied Water, L/kg | 45 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 91 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 92 to 260 | |
| 180 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 12 to 13 | |
| 22 |
| Strength to Weight: Bending, points | 13 to 15 | |
| 20 |
| Thermal Shock Resistance, points | 10 to 12 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 2.0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 12 to 22 |
| Iron (Fe), % | 99.31 to 99.7 | |
| 0 to 24.5 |
| Manganese (Mn), % | 0.3 to 0.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 15 |
| Nickel (Ni), % | 0 | |
| 50 to 60 |
| Niobium (Nb), % | 0 | |
| 4.0 to 6.0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 1.0 |
| Tungsten (W), % | 0 | |
| 0.5 to 2.5 |