SAE-AISI 1010 Steel vs. ASTM A302 Alloy Steel

Both SAE-AISI 1010 steel and ASTM A302 alloy steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1010 steel and the bottom bar is ASTM A302 alloy steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 110
180 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22 to 31
20 to 23
Fatigue Strength, MPa 150 to 230
250 to 280
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 230 to 250
370 to 390
Tensile Strength: Ultimate (UTS), MPa 350 to 400
590 to 620
Tensile Strength: Yield (Proof), MPa 190 to 330
350 to 390

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 47
39 to 51
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
7.2 to 7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 14
8.2 to 8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.4 to 3.0
Density, g/cm3 7.9
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 1.4
1.5 to 1.6
Embodied Energy, MJ/kg 18
20 to 21
Embodied Water, L/kg 45
48 to 50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82 to 93
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 290
330 to 410
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 12 to 14
21 to 22
Strength to Weight: Bending, points 14 to 15
20 to 21
Thermal Diffusivity, mm2/s 13
10 to 14
Thermal Shock Resistance, points 11 to 13
17 to 18