SAE-AISI 1010 Steel vs. EN AC-46600 Aluminum

SAE-AISI 1010 steel belongs to the iron alloys classification, while EN AC-46600 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is SAE-AISI 1010 steel and the bottom bar is EN AC-46600 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 110
77
Elastic (Young's, Tensile) Modulus, GPa 190
72
Elongation at Break, % 22 to 31
1.1
Fatigue Strength, MPa 150 to 230
75
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
27
Tensile Strength: Ultimate (UTS), MPa 350 to 400
180
Tensile Strength: Yield (Proof), MPa 190 to 330
110

Thermal Properties

Latent Heat of Fusion, J/g 250
490
Maximum Temperature: Mechanical, °C 400
170
Melting Completion (Liquidus), °C 1470
620
Melting Onset (Solidus), °C 1430
560
Specific Heat Capacity, J/kg-K 470
890
Thermal Conductivity, W/m-K 47
130
Thermal Expansion, µm/m-K 12
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
29
Electrical Conductivity: Equal Weight (Specific), % IACS 14
94

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
10
Density, g/cm3 7.9
2.8
Embodied Carbon, kg CO2/kg material 1.4
7.8
Embodied Energy, MJ/kg 18
150
Embodied Water, L/kg 45
1080

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82 to 93
1.7
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 290
81
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 12 to 14
18
Strength to Weight: Bending, points 14 to 15
25
Thermal Diffusivity, mm2/s 13
51
Thermal Shock Resistance, points 11 to 13
8.1

Alloy Composition

Aluminum (Al), % 0
85.6 to 92.4
Carbon (C), % 0.080 to 0.13
0
Copper (Cu), % 0
1.5 to 2.5
Iron (Fe), % 99.18 to 99.62
0 to 0.8
Lead (Pb), % 0
0 to 0.25
Magnesium (Mg), % 0
0 to 0.35
Manganese (Mn), % 0.3 to 0.6
0.15 to 0.65
Nickel (Ni), % 0
0 to 0.35
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0
6.0 to 8.0
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0
0 to 0.15
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 1.0
Residuals, % 0
0 to 0.15