SAE-AISI 1012 Steel vs. EN 1.4104 Stainless Steel
Both SAE-AISI 1012 steel and EN 1.4104 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1012 steel and the bottom bar is EN 1.4104 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 21 to 31 | |
| 11 to 23 |
| Fatigue Strength, MPa | 150 to 230 | |
| 230 to 310 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 230 to 250 | |
| 400 to 450 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 400 | |
| 630 to 750 |
| Tensile Strength: Yield (Proof), MPa | 200 to 330 | |
| 350 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 860 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1440 |
| Melting Onset (Solidus), °C | 1420 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 53 | |
| 25 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.9 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.9 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 8.5 |
| Density, g/cm3 | 7.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.2 |
| Embodied Energy, MJ/kg | 18 | |
| 30 |
| Embodied Water, L/kg | 45 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 80 to 93 | |
| 77 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 300 | |
| 310 to 800 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 13 to 14 | |
| 23 to 27 |
| Strength to Weight: Bending, points | 14 to 15 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 14 | |
| 6.7 |
| Thermal Shock Resistance, points | 11 to 13 | |
| 22 to 27 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.15 | |
| 0.1 to 0.17 |
| Chromium (Cr), % | 0 | |
| 15.5 to 17.5 |
| Iron (Fe), % | 99.16 to 99.6 | |
| 78.8 to 84.1 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0.2 to 0.6 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0.15 to 0.35 |