SAE-AISI 1015 Steel vs. EN 1.7367 Steel

Both SAE-AISI 1015 steel and EN 1.7367 steel are iron alloys. They have 89% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1015 steel and the bottom bar is EN 1.7367 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20 to 32
18
Fatigue Strength, MPa 170 to 250
310
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 390 to 440
670
Tensile Strength: Yield (Proof), MPa 210 to 370
460

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
600
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
26
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
7.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 18
37
Embodied Water, L/kg 45
88

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 360
560
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 14 to 15
24
Strength to Weight: Bending, points 15 to 16
22
Thermal Diffusivity, mm2/s 14
6.9
Thermal Shock Resistance, points 12 to 14
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0.13 to 0.18
0.080 to 0.12
Chromium (Cr), % 0
8.0 to 9.5
Iron (Fe), % 99.13 to 99.57
87.3 to 90.3
Manganese (Mn), % 0.3 to 0.6
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0
0.2 to 0.5
Sulfur (S), % 0 to 0.050
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010