SAE-AISI 1015 Steel vs. EN 1.8872 Steel

Both SAE-AISI 1015 steel and EN 1.8872 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1015 steel and the bottom bar is EN 1.8872 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20 to 32
21
Fatigue Strength, MPa 170 to 250
310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 260 to 270
380
Tensile Strength: Ultimate (UTS), MPa 390 to 440
610
Tensile Strength: Yield (Proof), MPa 210 to 370
450

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 18
22
Embodied Water, L/kg 45
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 360
530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 14 to 15
22
Strength to Weight: Bending, points 15 to 16
20
Thermal Diffusivity, mm2/s 14
10
Thermal Shock Resistance, points 12 to 14
18

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0.13 to 0.18
0 to 0.18
Chromium (Cr), % 0
0 to 0.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 99.13 to 99.57
95.1 to 100
Manganese (Mn), % 0.3 to 0.6
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0 to 0.050
0 to 0.0080
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.050