SAE-AISI 1015 Steel vs. C67300 Bronze

SAE-AISI 1015 steel belongs to the iron alloys classification, while C67300 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1015 steel and the bottom bar is C67300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 20 to 32
12
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 73
41
Shear Strength, MPa 260 to 270
300
Tensile Strength: Ultimate (UTS), MPa 390 to 440
500
Tensile Strength: Yield (Proof), MPa 210 to 370
340

Thermal Properties

Latent Heat of Fusion, J/g 250
190
Maximum Temperature: Mechanical, °C 400
130
Melting Completion (Liquidus), °C 1470
870
Melting Onset (Solidus), °C 1420
830
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 52
95
Thermal Expansion, µm/m-K 12
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
22
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
25

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
23
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 1.4
2.7
Embodied Energy, MJ/kg 18
46
Embodied Water, L/kg 45
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 110
55
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 360
550
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 14 to 15
17
Strength to Weight: Bending, points 15 to 16
17
Thermal Diffusivity, mm2/s 14
30
Thermal Shock Resistance, points 12 to 14
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.25
Carbon (C), % 0.13 to 0.18
0
Copper (Cu), % 0
58 to 63
Iron (Fe), % 99.13 to 99.57
0 to 0.5
Lead (Pb), % 0
0.4 to 3.0
Manganese (Mn), % 0.3 to 0.6
2.0 to 3.5
Nickel (Ni), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0
0.5 to 1.5
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
27.2 to 39.1
Residuals, % 0
0 to 0.5