SAE-AISI 1017 Steel vs. Nickel 333
SAE-AISI 1017 steel belongs to the iron alloys classification, while nickel 333 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1017 steel and the bottom bar is nickel 333.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 20 to 30 | |
| 34 |
| Fatigue Strength, MPa | 170 to 270 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 81 |
| Shear Strength, MPa | 280 to 290 | |
| 420 |
| Tensile Strength: Ultimate (UTS), MPa | 420 to 460 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 220 to 390 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1010 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 53 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.9 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.9 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 55 |
| Density, g/cm3 | 7.9 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 8.5 |
| Embodied Energy, MJ/kg | 18 | |
| 120 |
| Embodied Water, L/kg | 45 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 88 to 110 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 400 | |
| 180 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 15 to 16 | |
| 21 |
| Strength to Weight: Bending, points | 16 to 17 | |
| 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 2.9 |
| Thermal Shock Resistance, points | 13 to 14 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.15 to 0.2 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 24 to 27 |
| Cobalt (Co), % | 0 | |
| 2.5 to 4.0 |
| Iron (Fe), % | 99.11 to 99.55 | |
| 9.3 to 24.5 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 4.0 |
| Nickel (Ni), % | 0 | |
| 44 to 48 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 2.5 to 4.0 |