SAE-AISI 1018 Steel vs. ASTM A203 Steel
Both SAE-AISI 1018 steel and ASTM A203 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1018 steel and the bottom bar is ASTM A203 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 130 to 140 | |
160 to 180 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 17 to 27 | |
22 to 26 |
Fatigue Strength, MPa | 180 to 270 | |
210 to 280 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
73 |
Shear Strength, MPa | 280 to 300 | |
330 to 370 |
Tensile Strength: Ultimate (UTS), MPa | 430 to 480 | |
520 to 590 |
Tensile Strength: Yield (Proof), MPa | 240 to 400 | |
290 to 390 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Maximum Temperature: Mechanical, °C | 400 | |
410 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 52 | |
52 |
Thermal Expansion, µm/m-K | 12 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
7.4 to 7.6 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
8.5 to 8.7 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.8 | |
3.2 to 4.0 |
Density, g/cm3 | 7.9 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.6 to 1.7 |
Embodied Energy, MJ/kg | 18 | |
21 to 23 |
Embodied Water, L/kg | 46 | |
50 to 52 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 75 to 100 | |
110 to 120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 430 | |
230 to 410 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 15 to 17 | |
18 to 21 |
Strength to Weight: Bending, points | 16 to 17 | |
18 to 20 |
Thermal Diffusivity, mm2/s | 14 | |
14 |
Thermal Shock Resistance, points | 14 to 15 | |
15 to 17 |