SAE-AISI 1018 Steel vs. Type 1 Niobium
SAE-AISI 1018 steel belongs to the iron alloys classification, while Type 1 niobium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1018 steel and the bottom bar is Type 1 niobium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 to 140 | |
| 79 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 17 to 27 | |
| 29 |
| Poisson's Ratio | 0.29 | |
| 0.4 |
| Shear Modulus, GPa | 73 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 480 | |
| 140 |
| Tensile Strength: Yield (Proof), MPa | 240 to 400 | |
| 82 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 52 | |
| 52 |
| Thermal Expansion, µm/m-K | 12 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 8.6 |
| Embodied Water, L/kg | 46 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 75 to 100 | |
| 35 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 430 | |
| 32 |
| Stiffness to Weight: Axial, points | 13 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 15 to 17 | |
| 4.6 |
| Strength to Weight: Bending, points | 16 to 17 | |
| 7.1 |
| Thermal Diffusivity, mm2/s | 14 | |
| 23 |
| Thermal Shock Resistance, points | 14 to 15 | |
| 13 |
Alloy Composition
| Carbon (C), % | 0.15 to 0.2 | |
| 0 to 0.010 |
| Hafnium (Hf), % | 0 | |
| 0 to 0.020 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 98.8 to 99.25 | |
| 0 to 0.0050 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.010 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0050 |
| Niobium (Nb), % | 0 | |
| 99.7 to 100 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.015 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Tungsten (W), % | 0 | |
| 0 to 0.030 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |