SAE-AISI 1022 Steel vs. EN 1.1221 Steel

Both SAE-AISI 1022 steel and EN 1.1221 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1022 steel and the bottom bar is EN 1.1221 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 160
210 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 26
10 to 21
Fatigue Strength, MPa 190 to 300
240 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 310 to 340
450 to 520
Tensile Strength: Ultimate (UTS), MPa 480 to 550
730 to 870
Tensile Strength: Yield (Proof), MPa 260 to 450
390 to 550

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
48
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 18
19
Embodied Water, L/kg 46
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88 to 110
67 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 530
410 to 800
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17 to 19
26 to 31
Strength to Weight: Bending, points 17 to 19
23 to 26
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 15 to 17
23 to 28

Alloy Composition

Carbon (C), % 0.18 to 0.23
0.57 to 0.65
Chromium (Cr), % 0
0 to 0.4
Iron (Fe), % 98.7 to 99.12
97.1 to 98.8
Manganese (Mn), % 0.7 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0 to 0.050
0 to 0.035