SAE-AISI 1022 Steel vs. EN 1.4598 Stainless Steel

Both SAE-AISI 1022 steel and EN 1.4598 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1022 steel and the bottom bar is EN 1.4598 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 160
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17 to 26
46
Fatigue Strength, MPa 190 to 300
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 310 to 340
420
Tensile Strength: Ultimate (UTS), MPa 480 to 550
600
Tensile Strength: Yield (Proof), MPa 260 to 450
230

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
950
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
19
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.8
Embodied Energy, MJ/kg 18
52
Embodied Water, L/kg 46
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88 to 110
220
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 530
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 19
21
Strength to Weight: Bending, points 17 to 19
20
Thermal Diffusivity, mm2/s 14
4.1
Thermal Shock Resistance, points 15 to 17
14

Alloy Composition

Carbon (C), % 0.18 to 0.23
0 to 0.030
Chromium (Cr), % 0
16.5 to 18.5
Copper (Cu), % 0
1.3 to 1.8
Iron (Fe), % 98.7 to 99.12
60.8 to 70.1
Manganese (Mn), % 0.7 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 0
10 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.050
0.1 to 0.2