SAE-AISI 1022 Steel vs. EN 1.7365 Steel
Both SAE-AISI 1022 steel and EN 1.7365 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1022 steel and the bottom bar is EN 1.7365 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 150 to 160 | |
210 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 17 to 26 | |
18 |
Fatigue Strength, MPa | 190 to 300 | |
320 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
74 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 550 | |
700 |
Tensile Strength: Yield (Proof), MPa | 260 to 450 | |
470 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
260 |
Maximum Temperature: Mechanical, °C | 400 | |
510 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 52 | |
40 |
Thermal Expansion, µm/m-K | 12 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
8.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
9.4 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.8 | |
4.4 |
Density, g/cm3 | 7.9 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.8 |
Embodied Energy, MJ/kg | 18 | |
24 |
Embodied Water, L/kg | 46 | |
70 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 88 to 110 | |
110 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 530 | |
580 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 17 to 19 | |
25 |
Strength to Weight: Bending, points | 17 to 19 | |
22 |
Thermal Diffusivity, mm2/s | 14 | |
11 |
Thermal Shock Resistance, points | 15 to 17 | |
20 |
Alloy Composition
Carbon (C), % | 0.18 to 0.23 | |
0.12 to 0.19 |
Chromium (Cr), % | 0 | |
4.0 to 6.0 |
Copper (Cu), % | 0 | |
0 to 0.3 |
Iron (Fe), % | 98.7 to 99.12 | |
91.2 to 94.9 |
Manganese (Mn), % | 0.7 to 1.0 | |
0.5 to 0.8 |
Molybdenum (Mo), % | 0 | |
0.45 to 0.65 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.025 |
Silicon (Si), % | 0 | |
0 to 0.8 |
Sulfur (S), % | 0 to 0.050 | |
0 to 0.025 |
Vanadium (V), % | 0 | |
0 to 0.050 |