SAE-AISI 1035 Steel vs. ASTM A182 Grade F10
Both SAE-AISI 1035 steel and ASTM A182 grade F10 are iron alloys. They have 70% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1035 steel and the bottom bar is ASTM A182 grade F10.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 180 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 13 to 21 | |
| 34 |
| Fatigue Strength, MPa | 210 to 340 | |
| 180 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 40 to 45 | |
| 56 |
| Shear Modulus, GPa | 73 | |
| 74 |
| Shear Strength, MPa | 360 to 370 | |
| 420 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 620 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 300 to 530 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 600 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1420 |
| Melting Onset (Solidus), °C | 1420 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 18 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.6 |
| Embodied Energy, MJ/kg | 18 | |
| 51 |
| Embodied Water, L/kg | 46 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 to 99 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 740 | |
| 140 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 22 | |
| 22 |
| Strength to Weight: Bending, points | 19 to 21 | |
| 21 |
| Thermal Shock Resistance, points | 18 to 20 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.38 | |
| 0.1 to 0.2 |
| Chromium (Cr), % | 0 | |
| 7.0 to 9.0 |
| Iron (Fe), % | 98.6 to 99.08 | |
| 66.5 to 72.4 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.5 to 0.8 |
| Nickel (Ni), % | 0 | |
| 19 to 22 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 1.0 to 1.4 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.030 |