SAE-AISI 1035 Steel vs. ASTM A229 Spring Steel
Both SAE-AISI 1035 steel and ASTM A229 spring steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1035 steel and the bottom bar is ASTM A229 spring steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 180 | |
| 490 to 550 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 13 to 21 | |
| 14 |
| Fatigue Strength, MPa | 210 to 340 | |
| 710 to 790 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 360 to 370 | |
| 1020 to 1140 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 620 | |
| 1690 to 1890 |
| Tensile Strength: Yield (Proof), MPa | 300 to 530 | |
| 1100 to 1230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 50 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 19 |
| Embodied Water, L/kg | 46 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 to 99 | |
| 200 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 740 | |
| 3260 to 4080 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 22 | |
| 60 to 67 |
| Strength to Weight: Bending, points | 19 to 21 | |
| 40 to 43 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 18 to 20 | |
| 54 to 60 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.38 | |
| 0.55 to 0.85 |
| Iron (Fe), % | 98.6 to 99.08 | |
| 97.5 to 99 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.3 to 1.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.050 |