SAE-AISI 1035 Steel vs. EN 1.4034 Stainless Steel
Both SAE-AISI 1035 steel and EN 1.4034 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1035 steel and the bottom bar is EN 1.4034 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 13 to 21 | |
| 11 to 14 |
| Fatigue Strength, MPa | 210 to 340 | |
| 230 to 400 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 360 to 370 | |
| 420 to 540 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 620 | |
| 690 to 900 |
| Tensile Strength: Yield (Proof), MPa | 300 to 530 | |
| 390 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 770 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1440 |
| Melting Onset (Solidus), °C | 1420 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 51 | |
| 30 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 3.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 7.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.0 |
| Embodied Energy, MJ/kg | 18 | |
| 27 |
| Embodied Water, L/kg | 46 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 to 99 | |
| 81 to 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 740 | |
| 400 to 1370 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 to 22 | |
| 25 to 32 |
| Strength to Weight: Bending, points | 19 to 21 | |
| 22 to 27 |
| Thermal Diffusivity, mm2/s | 14 | |
| 8.1 |
| Thermal Shock Resistance, points | 18 to 20 | |
| 24 to 32 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.38 | |
| 0.43 to 0.5 |
| Chromium (Cr), % | 0 | |
| 12.5 to 14.5 |
| Iron (Fe), % | 98.6 to 99.08 | |
| 83 to 87.1 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.015 |