SAE-AISI 1038 Steel vs. 7076 Aluminum
SAE-AISI 1038 steel belongs to the iron alloys classification, while 7076 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is SAE-AISI 1038 steel and the bottom bar is 7076 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 180 | |
| 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 70 |
| Elongation at Break, % | 14 to 20 | |
| 6.2 |
| Fatigue Strength, MPa | 220 to 350 | |
| 170 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 27 |
| Shear Strength, MPa | 370 to 390 | |
| 310 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 640 | |
| 530 |
| Tensile Strength: Yield (Proof), MPa | 320 to 540 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 630 |
| Melting Onset (Solidus), °C | 1420 | |
| 460 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 860 |
| Thermal Conductivity, W/m-K | 51 | |
| 140 |
| Thermal Expansion, µm/m-K | 12 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 8.0 |
| Embodied Energy, MJ/kg | 18 | |
| 150 |
| Embodied Water, L/kg | 46 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 100 | |
| 31 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 790 | |
| 1510 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 45 |
| Strength to Weight: Axial, points | 21 to 23 | |
| 49 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 48 |
| Thermal Diffusivity, mm2/s | 14 | |
| 54 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 86.9 to 91.2 |
| Carbon (C), % | 0.35 to 0.42 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.3 to 1.0 |
| Iron (Fe), % | 98.6 to 99.05 | |
| 0 to 0.6 |
| Magnesium (Mg), % | 0 | |
| 1.2 to 2.0 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.3 to 0.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 7.0 to 8.0 |
| Residuals, % | 0 | |
| 0 to 0.15 |