SAE-AISI 1038 Steel vs. AISI 316 Stainless Steel
Both SAE-AISI 1038 steel and AISI 316 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1038 steel and the bottom bar is AISI 316 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 170 to 180 | |
160 to 360 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Elongation at Break, % | 14 to 20 | |
8.0 to 55 |
Fatigue Strength, MPa | 220 to 350 | |
210 to 430 |
Poisson's Ratio | 0.29 | |
0.28 |
Reduction in Area, % | 40 to 45 | |
80 |
Shear Modulus, GPa | 73 | |
78 |
Shear Strength, MPa | 370 to 390 | |
350 to 690 |
Tensile Strength: Ultimate (UTS), MPa | 590 to 640 | |
520 to 1180 |
Tensile Strength: Yield (Proof), MPa | 320 to 540 | |
230 to 850 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
290 |
Maximum Temperature: Mechanical, °C | 400 | |
590 |
Melting Completion (Liquidus), °C | 1460 | |
1400 |
Melting Onset (Solidus), °C | 1420 | |
1380 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 51 | |
15 |
Thermal Expansion, µm/m-K | 12 | |
16 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
2.3 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
2.6 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.8 | |
19 |
Density, g/cm3 | 7.8 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
3.9 |
Embodied Energy, MJ/kg | 18 | |
53 |
Embodied Water, L/kg | 46 | |
150 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 100 | |
85 to 260 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 790 | |
130 to 1820 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 21 to 23 | |
18 to 41 |
Strength to Weight: Bending, points | 20 to 21 | |
18 to 31 |
Thermal Diffusivity, mm2/s | 14 | |
4.1 |
Thermal Shock Resistance, points | 19 to 20 | |
11 to 26 |
Alloy Composition
Carbon (C), % | 0.35 to 0.42 | |
0 to 0.080 |
Chromium (Cr), % | 0 | |
16 to 18 |
Iron (Fe), % | 98.6 to 99.05 | |
62 to 72 |
Manganese (Mn), % | 0.6 to 0.9 | |
0 to 2.0 |
Molybdenum (Mo), % | 0 | |
2.0 to 3.0 |
Nickel (Ni), % | 0 | |
10 to 14 |
Nitrogen (N), % | 0 | |
0 to 0.1 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.045 |
Silicon (Si), % | 0 | |
0 to 0.75 |
Sulfur (S), % | 0 to 0.050 | |
0 to 0.030 |