SAE-AISI 1039 Steel vs. N08024 Nickel
SAE-AISI 1039 steel belongs to the iron alloys classification, while N08024 nickel belongs to the nickel alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1039 steel and the bottom bar is N08024 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 14 to 18 | |
| 34 |
| Fatigue Strength, MPa | 230 to 370 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Shear Strength, MPa | 380 to 420 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 610 to 690 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 340 to 580 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 990 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Conductivity, W/m-K | 51 | |
| 12 |
| Thermal Expansion, µm/m-K | 12 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 1.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 1.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 41 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 7.2 |
| Embodied Energy, MJ/kg | 18 | |
| 99 |
| Embodied Water, L/kg | 46 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 88 to 94 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 to 890 | |
| 180 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 24 | |
| 21 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 20 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.2 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0.37 to 0.44 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 22.5 to 25 |
| Copper (Cu), % | 0 | |
| 0.5 to 1.5 |
| Iron (Fe), % | 98.5 to 98.9 | |
| 26.6 to 38.4 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 5.0 |
| Nickel (Ni), % | 0 | |
| 35 to 40 |
| Niobium (Nb), % | 0 | |
| 0.15 to 0.35 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.035 |