SAE-AISI 1040 Steel vs. EN 1.6368 Steel
Both SAE-AISI 1040 steel and EN 1.6368 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1040 steel and the bottom bar is EN 1.6368 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 180 | |
| 200 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 13 to 20 | |
| 18 |
| Fatigue Strength, MPa | 220 to 340 | |
| 310 to 330 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 350 to 390 | |
| 410 to 430 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 640 | |
| 660 to 690 |
| Tensile Strength: Yield (Proof), MPa | 320 to 530 | |
| 460 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 40 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 3.4 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.7 |
| Embodied Energy, MJ/kg | 18 | |
| 22 |
| Embodied Water, L/kg | 46 | |
| 53 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 to 96 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 760 | |
| 580 to 650 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 23 | |
| 23 to 24 |
| Strength to Weight: Bending, points | 19 to 21 | |
| 21 to 22 |
| Thermal Diffusivity, mm2/s | 14 | |
| 11 |
| Thermal Shock Resistance, points | 18 to 20 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.015 to 0.040 |
| Carbon (C), % | 0.37 to 0.44 | |
| 0 to 0.17 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0.5 to 0.8 |
| Iron (Fe), % | 98.6 to 99.03 | |
| 95.1 to 97.2 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.8 to 1.2 |
| Molybdenum (Mo), % | 0 | |
| 0.25 to 0.5 |
| Nickel (Ni), % | 0 | |
| 1.0 to 1.3 |
| Niobium (Nb), % | 0 | |
| 0.015 to 0.045 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0.25 to 0.5 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.010 |