SAE-AISI 1042 Steel vs. EN 1.4303 Stainless Steel
Both SAE-AISI 1042 steel and EN 1.4303 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1042 steel and the bottom bar is EN 1.4303 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 200 | |
| 190 to 270 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 14 to 18 | |
| 13 to 49 |
| Fatigue Strength, MPa | 230 to 370 | |
| 220 to 320 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 380 to 420 | |
| 420 to 540 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 700 | |
| 590 to 900 |
| Tensile Strength: Yield (Proof), MPa | 340 to 580 | |
| 230 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 940 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1420 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 52 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 17 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.2 |
| Embodied Energy, MJ/kg | 18 | |
| 46 |
| Embodied Water, L/kg | 46 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 94 | |
| 110 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 to 900 | |
| 140 to 800 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 21 to 32 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 20 to 26 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.0 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 13 to 20 |
Alloy Composition
| Carbon (C), % | 0.4 to 0.47 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 | |
| 17 to 19 |
| Iron (Fe), % | 98.5 to 99 | |
| 64.8 to 72 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 11 to 13 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.015 |