SAE-AISI 1042 Steel vs. S31277 Stainless Steel
Both SAE-AISI 1042 steel and S31277 stainless steel are iron alloys. They have 42% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1042 steel and the bottom bar is S31277 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 14 to 18 | |
| 45 |
| Fatigue Strength, MPa | 230 to 370 | |
| 380 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 80 |
| Shear Strength, MPa | 380 to 420 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 700 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 340 to 580 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 36 |
| Density, g/cm3 | 7.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 6.7 |
| Embodied Energy, MJ/kg | 18 | |
| 90 |
| Embodied Water, L/kg | 46 | |
| 220 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 94 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 to 900 | |
| 410 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 29 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 25 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.4 to 0.47 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 | |
| 20.5 to 23 |
| Copper (Cu), % | 0 | |
| 0.5 to 1.5 |
| Iron (Fe), % | 98.5 to 99 | |
| 35.5 to 46.2 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 3.0 |
| Molybdenum (Mo), % | 0 | |
| 6.5 to 8.0 |
| Nickel (Ni), % | 0 | |
| 26 to 28 |
| Nitrogen (N), % | 0 | |
| 0.3 to 0.4 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.010 |